ABS Qimei Zhangzhou PA‑707K
Product Introduction ABS Qimei Zhangzhou PA‑707K is a general‑purpose ABS resin with high gloss, ultra‑high rigidity and excellent flexural strength. It is mainly processed by injection molding, suitable for manufacturing consumer goods and electronic‑electrical components requiring surface gloss and structural strength.
Main Applications
Electronic‑Electrical Housings: Telephone housings, home‑appliance buttons and other parts.
Consumer Goods: Toys, office supplies, clock housings, lamp bases and other products.
Physical Properties
| Property Category |
Test Item |
Test Condition / Standard |
Typical Value |
Unit |
| Physical Properties |
Density |
23°C, ISO 1183 |
1.05 |
g/cm³ |
| |
Melt Volume Flow Rate(MVR) |
200°C/5.0 kg, ISO 1133 |
2.10 |
cm³/10min |
| |
Melt Volume Flow Rate(MVR) |
220°C/10.0 kg, ISO 1133 |
23 |
cm³/10min |
Mechanical Properties
| Property Category |
Test Item |
Test Condition / Standard |
Typical Value |
Unit |
| Mechanical Properties |
Tensile Strength (Yield) |
23°C, ISO 527‑2 |
48 |
MPa |
| |
Elongation at Break |
23°C, ISO 527‑2 |
20 |
% |
| |
Flexural Strength |
23°C, ISO 178 |
73 |
MPa |
| |
Charpy Notched Impact Strength |
23°C, ISO 179/1eA |
16 |
kJ/m² |
| |
Izod Unnotched Impact Strength |
23°C, ISO 180/1U |
15 |
kJ/m² |
| |
Rockwell Hardness |
R‑Scale, ASTM D785 |
R116 |
R‑scale |
Thermal Properties
| Property Category |
Test Item |
Test Condition / Standard |
Typical Value |
Unit |
| Thermal Properties |
Heat‑Distortion Temperature (HDT) |
1.8 MPa, Unannealed, ISO 75‑2/Af |
83 |
°C |
| |
Heat‑Distortion Temperature (HDT) |
1.8 MPa, Annealed, ISO 75‑2/A |
98 |
°C |
| |
Vicat Softening Temperature |
10N,50°C/h, ISO 306/A50 |
104 |
°C |
Other Properties
| Property Category |
Test Item |
Test Condition / Standard |
Typical Value |
Unit |
| Other Properties |
Flammability Rating |
UL94,1.5 mm |
HB |
‑ |
Injection‑Molding Parameters
| Processing Parameter |
Suggested Value / Range |
Unit |
| Drying Temperature |
80‑85 |
°C |
| Drying Time |
2‑4 |
h |
| Barrel‑Rear Temperature |
180‑220 |
°C |
| Barrel‑Middle Temperature |
190‑230 |
°C |
| Barrel‑Front Temperature |
190‑230 |
°C |
| Nozzle Temperature |
185‑235 |
°C |
| Mold Temperature |
30‑70 (or 60‑65) |
°C |
| Melt Temperature |
220‑260 (250 preferred) |
°C |
| Injection Pressure |
60‑130 |
kg/cm² |
| Holding Pressure |
20‑50 |
kg/cm² |
| Back Pressure |
5‑7 |
MPa |
| Screw Speed |
30‑100 |
rpm |
Note: All data above is for reference only.