ABS CHIMEI Taiwan PA‑765A

Product Introduction ABS CHIMEI Taiwan PA‑765A is an injection‑molding‑grade ABS resin with high flowability and excellent flame‑retardant performance. Featuring favorable comprehensive properties, it is especially suitable for manufacturing thin‑wall, complex‑structure components requiring high flame‑retardant requirements.

Main Applications

Electronic‑Electrical Equipment: Monitor housings, power sockets, charger shells, router / set‑top‑box housings.

Office & Commercial Equipment: Printers, fax machines, projectors, cash‑register housings, electric‑meter housings.

Home Appliances: TV frames, coffee‑machine housings, home‑appliance control panels.

Industrial & Automotive Parts: Power‑tool accessories, car‑audio panels, automotive‑battery assemblies, motorcycle accessories.

Physical Properties

Property Category	Test Item	Test Condition / Standard	Typical Value / Range	Unit
Physical Properties	Density	23°C, ASTM D792	1.17	g/cm³
	Melt Flow Rate (MFR)	200°C/5.0 kg, ASTM D1238	4.6‑4.8	g/10min
	Melt Flow Rate (MFR)	220°C/10.0 kg, ASTM D1238	46‑55	g/10min

Mechanical Properties

Property Category	Test Item	Test Condition / Standard	Typical Value / Range	Unit
Mechanical Properties	Tensile Strength (Yield)	ASTM D638	39.1‑40.0	MPa
	Tensile Strength (Break)	ISO 527‑2/50	28.0‑29.0	MPa
	Elongation at Break	ASTM D638	15‑20	%
	Flexural Strength	ASTM D790	62.5‑62.8	MPa
	Flexural Modulus	ASTM D790	2210‑2260	MPa
	Izod Notched Impact Strength	1/4",23°C, ASTM D256	17‑21 or 200‑230	kg·cm/cm J/m
	Charpy Notched Impact Strength	23°C, ISO 179/1eA	20‑24	kJ/m²
	Rockwell Hardness	R‑Scale, ASTM D785	R100‑R101	R‑scale

Thermal Properties

Property Category	Test Item	Test Condition / Standard	Typical Value / Range	Unit
Thermal Properties	Heat‑Distortion Temperature (HDT)	1.8 MPa, Unannealed, ASTM D648	76.0	°C
	Heat‑Distortion Temperature (HDT)	1.8 MPa, Annealed, ASTM D648	85.0	°C
	Vicat Softening Temperature	ASTM D1525	92.0	°C

Flame‑Retardant Properties

Property Category	Test Item	Test Condition / Standard	Typical Value / Range	Unit
Flame‑Retardant Properties	Flammability Rating	UL94,1.5mm/2.0mm/2.1mm	V‑0	‑
	Flammability Rating	UL94,2.5mm	5VA	‑

Injection‑Molding Parameters

Processing Parameter	Suggested Value / Range	Unit
Drying Temperature	80‑85	°C
Drying Time	2‑4 (or 3)	h
Barrel‑Rear Temperature	180‑220	°C
Barrel‑Middle Temperature	190‑230	°C
Barrel‑Front Temperature	190‑230	°C
Nozzle Temperature	185‑235	°C
Mold Temperature	40‑80 (commonly 40‑70)	°C
Melt Temperature	220‑250	°C
Injection Pressure	60‑130 (or 100‑150)	MPa (or kg/cm²)
Holding Pressure	30%‑60% of injection pressure	MPa (or kg/cm²)
Back Pressure	5‑15	MPa (or kg/cm²)
Screw Speed	Max linear velocity 0.6 m/s	rpm
Injection Speed	Graded injection, slow‑to‑fast	‑

Note: All data above is for reference only.