ABS Dagusi Tianjin DG‑417
ABS Dagusi Tianjin DG‑417
Product Introduction ABS Dagusi Tianjin DG‑417 is a highly versatile injection‑molding ABS resin. With high gloss, high rigidity and good comprehensive performance, it is widely used in many industries.
Main Applications
Electronic‑Electrical Housings: Housings for televisions, copiers, telephones and other equipment.
Automotive Parts: Instrument panels, door panels, bumpers, wheel‑cover parts and other components.
Consumer Goods: Cosmetic cases, containers, toys, office supplies, household articles.
Other Applications: Power‑tool accessories, general mechanical parts, transmission parts and telecommunication components.
Performance Parameters
| Property Category | Test Item | Test Condition / Standard | Typical Value / Range | Unit |
|---|---|---|---|---|
| Physical Properties | Density | 23°C, ASTM D792 | 1.04‑1.05 | g/cm³ |
| Melt Flow Rate (MFR) | 220°C/10.0 kg, ASTM D1238 | 15.5‑20.0 | g/10min | |
| Molding Shrinkage | ASTM D955 | 0.4‑0.8 | % | |
| Mechanical Properties | Tensile Strength | ASTM D638 | 41.2‑52.0 (≈420‑510) | MPa (kgf/cm²) |
| Flexural Strength | ASTM D790 | 61.8‑85.3 (≈630‑870) | MPa (kgf/cm²) | |
| Flexural Modulus | ASTM D790 | 2060‑2468 (≈21000‑25180) | MPa (kgf/cm²) | |
| Izod Notched Impact Strength | 1/4",23°C, ASTM D256 | 18‑25 | kg·cm/cm or J/m | |
| Rockwell Hardness | R‑Scale, ASTM D785 | R109‑R112 | R‑scale | |
| Elongation at Break | ASTM D638 | 20‑40 | % | |
| Thermal Properties | Heat‑Deflection Temperature (HDT) | 1.8 MPa, unannealed, ASTM D648 | 80‑88 | °C |
| Vicat Softening Temperature | ASTM D1525 | 99‑105 | °C | |
| Other Properties | Flammability Rating | UL94,1.5 mm/1.6 mm | HB | ‑ |
Injection‑Molding Parameters
| Process Parameter | Recommended Range | Unit |
|---|---|---|
| Drying Temperature | 80‑90 | °C |
| Drying Time | 2‑4 (2‑3 hours minimum recommended) | h |
| Barrel‑Rear Temperature | 180‑220 | °C |
| Barrel‑Middle Temperature | 190‑230 | °C |
| Barrel‑Front Temperature | 190‑230 | °C |
| Nozzle Temperature | 185‑235 | °C |
| Mold Temperature | 40‑80 (commonly 50‑80) | °C |
| Melt Temperature | 200‑240 | °C |
| Injection Pressure | Customized according to product structure | MPa |
| Holding Pressure | Customized according to product structure | MPa |
| Back Pressure | Customized according to product structure | MPa |
| Screw Speed | Customized according to product structure | rpm |
Note: All data above is for reference only.