ABS CHIMEI Zhenjiang D‑1200

Product Introduction ABS CHIMEI Zhenjiang D‑1200 is a flame‑retardant general‑purpose ABS resin belonging to TBBA flame‑retardant series. It delivers favorable flame‑retardant performance, high rigidity and balanced mechanical properties, mainly processed by injection molding.

Main Applications

Electronic‑Electrical Equipment: Monitors, set‑top boxes, modems, power‑switch panels, power sockets, printer housings, remote controllers, fax machines, projectors, large‑size office machines, coffee‑machine housings, TV front & rear frames, DVD players, car‑audio control panels and other parts.

Automotive Field: Automotive‑battery housings and related components.

Commercial Equipment & Others: Cash‑register housings, electric‑meter housings, light‑box housings.

Performance Parameters

Property Category	Test Item	Test Condition / Standard	Typical / Range Value	Unit
Physical Properties	Density	23°C, ASTM D792	1.17	g/cm³
	Melt Flow Rate (MFR)	200°C/5.0 kg, ASTM D1238	5.0	g/10min
Mechanical Properties	Tensile Strength	ASTM D638	460 (≈45.1)	kgf/cm² (MPa)
	Flexural Strength	ASTM D790	750 (≈73.5)	kgf/cm² (MPa)
	Flexural Modulus	ASTM D790	26700 (≈2.62)	kgf/cm² (GPa)
	Izod Notched Impact Strength	1/4",23°C, ASTM D256	20	kg·cm/cm
	Rockwell Hardness	R‑Scale, ASTM D785	R103	R‑scale
	Elongation at Break	‑	20	%
Thermal Properties	Heat‑Deflection Temperature (HDT)	1.8 MPa, ASTM D648	80	°C
Flame‑Retardant Properties	Flammability Rating	UL94,1.5 mm	V‑2	‑
	Flammability Rating	UL94,2.5 mm	V‑0 / 5VB	‑
	Flammability Rating	UL94,3.0 mm	5VA	‑

Injection‑Molding Parameters

Process Parameter	Recommended Range / Description	Unit
Drying Temperature	80	°C
Drying Time	2‑3	h
Barrel‑Rear Temperature	180‑210	°C
Barrel‑Middle Temperature	190‑220	°C
Barrel‑Front / Nozzle Temperature	190‑220	°C
Mold Temperature	40‑70	°C
Injection Pressure	50‑60	kg/cm²
Holding Pressure	40‑50	kg/cm²
Back Pressure	5‑10	kg/cm²

Note: All data above is for reference only.