ABS CHIMEI Zhenjiang D‑1000
ABS CHIMEI Zhenjiang D‑1000
Product Introduction ABS CHIMEI Zhenjiang D‑1000 is a flame‑retardant general‑purpose ABS resin. It achieves UL94 V‑0 at 1.5 mm thickness and 5VA at 1/8" thickness. With good heat resistance and processing performance, it is suitable for electronic‑electrical products, office‑equipment parts and automotive components requiring flame‑retardant performance.
Main Applications
Electronic & Electrical Equipment: Monitors, set‑top boxes, modems, power‑switch panels, power sockets and other components.
Office & Commercial Equipment: Cash‑register housings, electric‑meter housings, printer housings, remote controllers, fax machines, projectors and large‑scale office machines.
Home Appliances: TV front‑rear frames, DVD players, automotive‑audio control panels, coffee‑machine housings.
Automotive Components: Automotive‑battery related parts.
Performance Parameters
| Property Category | Test Item | Test Condition / Standard | Typical / Range Value | Unit |
|---|---|---|---|---|
| Physical Properties | Density | 23°C, ASTM D792 | 1.17‑1.19 | g/cm³ |
| Melt Flow Rate (MFR) | 200°C/5.0 kg, ASTM D1238 | 4.6‑5.5 | g/10min | |
| Mechanical Properties | Tensile Strength (Yield) | ASTM D638 | 39.1‑42.6 | MPa |
| Tensile Strength (Break) | ISO 527‑2/50 | 28.0‑37.0 | MPa | |
| Elongation at Break | ASTM D638 | 15‑20 | % | |
| Flexural Strength | ASTM D790 | 62.5‑70.1 | MPa | |
| Flexural Modulus | ASTM D790 | 2210‑2350 | MPa | |
| Izod Notched Impact Strength | 1/4",23°C, ASTM D256 | 17‑21 or 200‑230 |
kg·cm/cm J/m |
|
| Charpy Notched Impact Strength | 23°C, ISO 179/1eA | 18‑20 | kJ/m² | |
| Rockwell Hardness | R‑Scale, ASTM D785 | R100‑R102 | ‑ | |
| Thermal Properties | Heat‑Deflection Temperature (HDT) | 1.8 MPa, unannealed, ASTM D648 | 76.0‑88.0 | °C |
| Heat‑Deflection Temperature (HDT) | 1.8 MPa, annealed, ASTM D648 | 85.0‑99.0 | °C | |
| Vicat Softening Temperature | ASTM D1525 | 92.0‑105.0 | °C | |
| Flame‑Retardant Properties | Flammability Rating | UL94,1.5 mm/2.0 mm/2.1 mm | V‑0 | ‑ |
| Flammability Rating | UL94,2.5 mm | 5VA | ‑ |
Injection‑Molding Parameters
| Process Parameter | Recommended Range | Unit |
|---|---|---|
| Drying Temperature | 80‑85 | °C |
| Drying Time | 2‑4 (3 hours recommended) | h |
| Barrel‑Rear Temperature | 180‑220 | °C |
| Barrel‑Middle Temperature | 190‑230 | °C |
| Barrel‑Front Temperature | 190‑230 | °C |
| Nozzle Temperature | 185‑235 | °C |
| Mold Temperature | 40‑80 (commonly 40‑70) | °C |
| Melt Temperature | 220‑250 | °C |
| Injection Pressure | 60‑130 (or 100‑150) | MPa (or kg/cm²) |
| Holding Pressure | 20‑50 (30%‑60% of injection pressure) | MPa (or kg/cm²) |
| Back Pressure | 5‑15 | MPa (or kg/cm²) |
| Screw Speed | 30‑100(max 0.6 m/s linear velocity) | rpm |
Note: All data above is for reference only.