ABS CHIMEI Zhenjiang D‑1400
ABS CHIMEI Zhenjiang D‑1400
Product Introduction ABS CHIMEI Zhenjiang D‑1400 is a flame‑retardant ABS resin (TBBA series). It obtains UL94 V‑0 certification at 3.0 mm thickness, featuring good heat resistance and processing performance. Mainly processed by injection molding, it is suitable for electronic‑electrical products, office‑equipment parts and automotive components requiring flame‑retardant performance.
Main Applications
Electronic & Electrical Equipment: Monitors, set‑top boxes, modems, power‑switch panels, power sockets.
Office & Commercial Equipment: Cash‑register housings, electric‑meter housings, printer housings, remote controllers, fax machines, projectors and large‑scale office machines.
Home Appliances: TV front & rear frames, DVD players, automotive‑audio control panels, coffee‑machine housings and other parts.
Automotive Components: Automotive‑battery related parts.
Other Applications: Light‑box housings and other end‑products.
Performance Parameters
| Property Category | Test Item | Test Condition / Standard | Typical / Range Value | Unit |
|---|---|---|---|---|
| Physical Properties | Density | 23°C, ISO 1183 | 1.15 | g/cm³ |
| Melt Volume Flow Rate(MVR) | 200°C/5.0 kg, ISO 1133 | 4.0 | cm³/10min | |
| Melt Volume Flow Rate(MVR) | 220°C/10.0 kg, ISO 1133 | 42 | cm³/10min | |
| Mechanical Properties | Tensile Strength | 50 mm/min, ISO 527 | 40 | MPa |
| Elongation at Break | 50 mm/min, ISO 527 | 25 | % | |
| Flexural Strength | 2 mm/min, ISO 178 | 64 | MPa | |
| Flexural Modulus | 2 mm/min, ISO 178 | 2200 | MPa | |
| Charpy Notched Impact Strength | 23°C, ISO 179 | 22 | kJ/m² | |
| Izod Notched Impact Strength | 1/4",23°C, ASTM D256 | 22 | kg·cm/cm | |
| Rockwell Hardness | R‑Scale, ASTM D785 | 103 | R | |
| Thermal Properties | Heat‑Deflection Temperature (HDT) | 1.8 MPa, annealed, ISO 75‑2/A | 85 | °C |
| Heat‑Deflection Temperature (HDT) | 1.8 MPa, unannealed, ISO 75‑2/Af | 75 | °C | |
| Vicat Softening Temperature | 10N,50°C/hr, ISO 306 | 94 | °C | |
| Flame‑Retardant Properties | Flammability Rating | UL94,3.0 mm | V‑0 | ‑ |
| Flammability Rating | UL94,2.0 mm | V‑2 | ‑ |
Injection‑Molding Parameters
| Process Parameter | Recommended Range / Description | Unit |
|---|---|---|
| Drying Temperature | 80 | °C |
| Drying Time | 2‑3 | h |
| Barrel‑Rear Temperature | 180‑210 | °C |
| Barrel‑Middle Temperature | 190‑220 | °C |
| Barrel‑Front / Nozzle Temperature | 190‑220 | °C |
| Mold Temperature | 40‑70 | °C |
| Injection Pressure | 50‑60 | kg/cm² |
| Holding Pressure | 40‑50 | kg/cm² |
| Back Pressure | 5‑10 | kg/cm² |
Note: All data above is for reference only.