Product Introduction ABS Zhejiang Petrochemical ZA0210 is a general‑purpose ABS resin with high gloss and high rigidity. Mainly processed by injection molding, it is suitable for components requiring high surface gloss and structural strength.

Main Applications

Electronics & Electrical: Housings for televisions, monitors, telephones, printers, home‑appliance buttons, electrical‑product housings and other electronic parts.

Automotive Components: Automotive interior and exterior trim parts.

Home Appliances: Refrigerator door handles, drawer guides, washing‑machine control‑panel frames, air‑conditioner outlet blades, vacuum‑cleaner housings and other components.

Consumer Goods: Toys, office stationery, household articles such as clothes hangers and plastic storage boxes.

Performance Parameters

Property Category	Test Item	Test Condition / Standard	Typical / Range Value	Unit
Physical Properties	Density	ASTM D792	1.04‑1.05	g/cm³
	Melt Flow Rate (MFR)	220°C/10.0 kg, GB/T 3682.1	18‑24	g/10min
	Molding Shrinkage	ASTM D955	0.4‑0.7	%
Mechanical Properties	Tensile Strength	GB/T 1040.2, 50 mm/min	47	MPa
	Flexural Strength	GB/T 9341, 2 mm/min	76	MPa
	Flexural Modulus	‑	≥2300	MPa
	Izod Notched Impact Strength	23°C, GB/T 1043.1	≥16	kJ/m²
	Rockwell Hardness	R‑Scale, ASTM D785	R105‑R110	‑
Thermal Properties	Heat‑Deflection Temperature (HDT)	1.8 MPa, ASTM D648	85‑92	°C
	Vicat Softening Temperature	GB/T 1633	≥95	°C
Other Properties	Flammability Rating	UL94, 1.5 mm	HB	‑

Injection‑Molding Parameters

Process Parameter	Recommended Range / Description	Unit
Drying Temperature	80‑85	°C
Drying Time	2‑4	h
Barrel‑Rear Temperature	180‑200	°C
Barrel‑Middle Temperature	190‑220	°C
Barrel‑Front Temperature	200‑240	°C
Nozzle Temperature	210‑230	°C
Mold Temperature	40‑70 (commonly 50‑80)	°C
Injection Pressure	60‑100	MPa
Holding Pressure	30‑50	MPa
Screw Speed	≤80	rpm
Back Pressure	5‑10	MPa

Note: All data above is for reference only.