ABS Jihua Jieyang (PetroChina) 0215A
ABS Jihua Jieyang (PetroChina) 0215A
Product Introduction ABS Jihua Jieyang (PetroChina) 0215A is a high‑gloss general‑purpose injection‑molding ABS resin. With balanced mechanical properties, good processing flowability and excellent surface appearance, it is widely used in various industries.
Main Applications
Benefiting from high gloss and balanced comprehensive performance: Automotive Components: Automotive interior and exterior trim parts.
Electronics & Electrical: Housings for televisions, computer monitors, telephones, copiers, home‑appliance buttons, electrical‑product housings and other electronic parts.
Consumer Goods: Toys, office stationery, household articles, cosmetic cases, lamp holders and other products.
Performance Parameters
| Property Category | Test Item | Test Condition / Standard | Typical / Range Value | Unit |
|---|---|---|---|---|
| Physical Properties | Density | 23°C, ASTM D792 | 1.04‑1.05 | g/cm³ |
| Melt Flow Rate (MFR) | 200°C/5.0 kg, ASTM D1238 | 16‑20 | g/10min | |
| Melt Flow Rate (MFR) | 220°C/10.0 kg, ASTM D1238 | To be confirmed | g/10min | |
| Molding Shrinkage | ASTM D955 | To be confirmed | % | |
| Mechanical Properties | Tensile Strength | ASTM D638 | 48‑52 | MPa |
| Flexural Strength | ASTM D790 | 82‑91 | MPa | |
| Flexural Modulus | ASTM D790 | 2500‑2850 | MPa | |
| Izod Notched Impact Strength | 1/4", 23°C, ASTM D256 | 185 | J/m | |
| Rockwell Hardness | R‑Scale, ASTM D785 | R107‑R112 | ‑ | |
| Elongation at Break | ASTM D638 | To be confirmed | % | |
| Thermal Properties | Heat‑Deflection Temperature (HDT) | 1.8 MPa, annealed, ASTM D648 | 89‑91 | °C |
| Vicat Softening Temperature | ASTM D1525 | To be confirmed | °C | |
| Surface Properties | Gloss | ‑ | 96 | % |
| Other Properties | Flammability Rating | UL94, 1.5 mm | HB | ‑ |
Injection‑Molding Parameters
| Process Parameter | Recommended Range / Description | Unit |
|---|---|---|
| Drying Temperature | 80 | °C |
| Drying Time | 2‑4 (minimum 2‑4) | h |
| Barrel‑Rear Temperature | 180‑200 | °C |
| Barrel‑Middle Temperature | 190‑220 | °C |
| Barrel‑Front Temperature | 200‑230 | °C |
| Nozzle Temperature | 210‑230 | °C |
| Mold Temperature | 40‑80 (commonly 50‑80) | °C |
| Injection Pressure | 60‑100 | MPa |
| Holding Pressure | 30‑50 | MPa |
| Screw Speed | 30‑70 | rpm |
Note: All data above is for reference only.