ABS Formosa Chemicals & Fibre (Ningbo) ANC160

Product Introduction ABS ANC160 is a flame‑retardant‑grade ABS resin with high gloss and high rigidity. It is mainly processed by injection molding, suitable for electronic‑electrical components requiring flame‑retardant performance and premium surface gloss.

Main Applications

Electronic & Electrical Equipment: Typical application field for ANC160. Widely used for housings of TV sets, computer monitors, copiers, printers, security‑equipment products, etc.

Home Appliances: Housings and components for small household appliances.

Automotive Components: Automotive interior trims.

Performance Parameters

Property Category	Test Item	Test Condition / Standard	Typical / Range Value	Unit
Physical Properties	Density	23°C, ASTM D792	1.04‑1.05	g/cm³
	Melt Flow Rate (MFR)	200°C/5.0 kg, ASTM D1238	4.1‑4.5	g/10min
Mechanical Properties	Tensile Strength	ASTM D638	39.0‑42.0	MPa
	Flexural Strength	ASTM D790	61.0‑67.0	MPa
	Flexural Modulus	ASTM D790	2160‑2450	MPa
	Izod Notched Impact Strength	23°C, ASTM D256	18.0‑25.0	kg·cm/cm
	Rockwell Hardness	R‑Scale, ASTM D785	R101	‑
	Elongation at Break	ASTM D638	20	%
Thermal Properties	Heat‑Deflection Temperature (HDT)	1.8 MPa, unannealed, ASTM D648	80.0‑82.0	°C
	Heat‑Deflection Temperature (HDT)	1.8 MPa, annealed, ASTM D648	85.0‑89.0	°C
	Vicat Softening Temperature	ASTM D1525	85.0‑90.0	°C
Flame‑Retardant Properties	Flammability Rating	UL94, 2.5 mm	V‑0	‑

Injection‑Molding Parameters

Process Parameter	Recommended Range / Description	Unit
Drying Temperature	70‑80	°C
Drying Time	2‑3	h
Barrel‑Rear Temperature	150‑190	°C
Barrel‑Middle Temperature	160‑200	°C
Barrel‑Front Temperature	170‑210	°C
Nozzle Temperature	180‑220	°C
Mold Temperature	40‑70	°C
Injection Pressure	58.8‑108	MPa
Melt Temperature	160‑200	°C

Note: All data above is for reference only.