ABS Lotte Chemical VH‑0810T

Product Introduction ABS Lotte Chemical VH‑0810T is a flame‑retardant‑grade ABS resin featuring high flowability and high gloss. It is mainly processed by injection molding, suitable for components requiring flame retardancy, good surface appearance and high processing efficiency.

Main Applications

Electronic & Electrical Equipment: Outer housings for OA equipment including TV sets, computer monitors, copiers, printers and fax machines.

Home Appliances: Components for small household appliances.

Automotive Components: Automotive interior trims.

Other Fields: Power‑tool parts, sports‑equipment components and other parts requiring mechanical strength and flame‑retardant performance.

Performance Parameters

Property Category	Test Item	Test Condition / Standard	Typical / Range Value	Unit
Physical Properties	Density	23°C, ASTM D792	1.16‑1.17	g/cm³
	Melt Flow Rate (MFR)	200°C/5.0 kg, ASTM D1238	6.0‑6.5	g/10min
	Molding Shrinkage (Flow direction)	3.2 mm, ASTM D955	0.28‑0.34	%
Mechanical Properties	Tensile Strength	ASTM D638	39	MPa
	Flexural Strength	ASTM D790	58.5‑59.0	MPa
	Flexural Modulus	ASTM D790	2135‑2160	MPa
	Izod Notched Impact Strength	23°C, ASTM D256	4.00 (0.125 in)	ft·lb/in
	Rockwell Hardness	R‑Scale, ASTM D785	101‑103	R‑scale
Thermal Properties	Heat‑Deflection Temperature (HDT)	1.8 MPa, unannealed, ASTM D648	71‑77	°C
	Vicat Softening Temperature	ASTM D1525 / ISO R 306	87‑90	°C
Flame‑Retardant Properties	Flammability Rating	UL94, 1.5 mm (0.059 in)	V‑2	‑
	Flammability Rating	UL94, 2.5 mm	V‑0	‑

Injection‑Molding Parameters

Process Parameter	Recommended Range / Description	Unit
Drying Temperature	80	°C
Drying Time	2‑4	h
Barrel‑Rear Temperature	180‑190	°C
Barrel‑Middle Temperature	190‑200	°C
Barrel‑Front Temperature	200‑210	°C
Nozzle Temperature	210‑220	°C
Mold Temperature	40‑80	°C
Injection Pressure	58.8‑108	MPa
Melt Temperature	200‑230	°C
Back Pressure	0.49‑1.96	MPa
Screw Speed	50‑150	rpm

Note: All data above is for reference only.