ABS Formosa Chemicals & Fibre (Ningbo) AG15E1‑H

Product Introduction ABS AG15E1‑H is a general‑purpose injection‑molding ABS resin with high rigidity and high gloss. It delivers balanced comprehensive performance, mainly used for daily‑use articles and electronic‑electrical components requiring good surface gloss and structural strength.

Main Applications

Electronic & Electrical Housings: Housings for telephones, computers, audio equipment and other products.

Consumer Goods: Toys, clock housings, luggage cases, shoe heels, office‑equipment parts and other articles.

Performance Parameters

Property Category	Test Item	Test Condition / Standard	Typical / Range Value	Unit
Physical Properties	Density	23°C, ASTM D792	1.05	g/cm³
	Melt Flow Rate (MFR)	200°C/5.0 kg, ASTM D1238	1.8	g/10min
	Melt Flow Rate (MFR)	220°C/10.0 kg, ASTM D1238	20	g/10min
Mechanical Properties	Tensile Strength	23°C, ASTM D638	52	MPa
	Flexural Strength	23°C, ASTM D790	85.3‑86.0	MPa
	Flexural Modulus	23°C, ASTM D790	2750‑28000	kg/cm² (MPa)
	Izod Notched Impact Strength	23°C, 1/4", ASTM D256	14	kg·cm/cm
	Rockwell Hardness	R‑Scale, ASTM D785	R110	‑
Thermal Properties	Heat‑Deflection Temperature (HDT)	1.8 MPa, unannealed, ASTM D648	84.0‑88.0	°C
	Heat‑Deflection Temperature (HDT)	1.8 MPa, annealed, ASTM D648	94.0‑100.0	°C
	Vicat Softening Temperature	ASTM D1525 / ISO 306	103	°C
Other Properties	Flammability Rating	UL94, 1.5 mm /1.6 mm	HB	‑

Injection‑Molding Parameters

Process Parameter	Recommended Range / Description	Unit
Drying Temperature	70‑80	°C
Drying Time	2‑3	h
Barrel‑Rear Temperature	190‑200	°C
Barrel‑Middle Temperature	200‑220	°C
Barrel‑Front Temperature	220‑230	°C
Nozzle Temperature	210‑230	°C
Mold Temperature	40‑80	°C
Injection Pressure	68.6‑108	MPa

Note: All data above is for reference only.