AS Chi Mei Taiwan PN‑117C
AS Chi Mei Taiwan PN‑117C
Product Introduction AS Chi Mei Taiwan PN‑117C resin is a high‑transparency, high‑flow acrylonitrile‑styrene copolymer (AS/SAN). It delivers good rigidity, heat resistance, chemical resistance and excellent processability.
Main Applications
Household Appliances: Mainly used for refrigerator vegetable‑fruit boxes and other daily‑use articles.
Daily‑use & Consumer Goods: Transparent household hardware, cosmetic cases, tableware, cups, toothbrush handles and pen barrels.
Electronic & Electrical Components: Electrical sockets, housings, instrument casings, dashboards, battery boxes, storage‑battery enclosures, junction boxes and transparent electrical panels.
Automotive Industry: Automotive parts including head‑lamp housings, rear‑view mirror housings and instrument panels.
Industrial & Other Articles: Oil‑resistant mechanical parts, tractor fuel tanks, packaging containers, filter pipes and building‑material products such as safety glass.
Performance Parameters
| Property Category | Test Item | Typical Value | Test Condition / Standard |
|---|---|---|---|
| Physical Properties | Density | 1.06 g/cm³ | ASTM D792, 23℃ |
| Melt Flow Rate (MFR) | 5.0 g/10min | 200°C / 5.0 kg, ASTM D1238 | |
| Melt Volume Rate (MVR) | 58.0 cm³/10min | 220°C / 10.0 kg, ISO 1133 | |
| Molding Shrinkage | 0.2‑0.7 % | ASTM D955 | |
| Mechanical Properties | Tensile Strength (Yield) | 65.7‑66.0 MPa | ASTM D638 / ISO 527‑2/50 |
| Flexural Strength | 89.0‑94.1 MPa | ASTM D790 / ISO 178 | |
| Flexural Modulus | 2700‑3330 MPa | ASTM D790 / ISO 178 | |
| Izod Notched Impact Strength | 17‑18 J/m (1/4") | ASTM D256, 23℃ | |
| Rockwell Hardness (M‑Scale) | M‑83 | ASTM D785 | |
| Elongation at Break | 3.0‑6.0 % | ASTM D638 / ISO 527‑2/50 | |
| Thermal Properties | Heat‑Deflection Temperature (HDT) | 89.0‑90.0 °C (un‑annealed); 100 °C (annealed) | 1.8 MPa, ASTM D648 / ISO 75‑2/A |
| Vicat Softening Temperature | 102‑109 °C | ISO 306 / ASTM D1525 | |
| Other Properties | Flammability (UL 94) | HB (1.6 mm) | UL 94 |
| Ball‑Indentation Hardness | 161 MPa | ISO 2039‑1 |
Injection‑Molding Parameters
| Process Parameter | Reference Range | Remarks & Instructions |
|---|---|---|
| Drying Treatment | 75‑80°C, 3‑4 hours | AS resin is hygroscopic. Sufficient drying is required (moisture content below 0.1% recommended), otherwise silver streaks and bubbles may occur on finished‑part surfaces. |
| Barrel Temperature | Feed zone:170‑180℃ | Compression zone:180‑200℃ | Metering zone:180‑210℃ | Nozzle:180‑210℃ | Prevent material degradation; avoid long‑term residence of molten material inside high‑temperature barrel. |
| Mold Temperature | 40‑60℃ | Suitable for high‑precision molded parts. Mold temperature directly affects appearance, shrinkage and internal stress of finished products. |
| Injection Pressure | 50‑70 kg/cm² | Adjust according to flow length and product structure. |
| Holding Pressure | 40‑60 kg/cm² | Approx.30%‑60% of injection pressure. Optimize according to wall thickness and product structure to reduce internal stress and shrinkage. |
| Back Pressure | 5‑15 kg/cm² | Proper back‑pressure ensures uniform plasticization and degassing. |
| Injection Speed | High‑speed injection recommended | Beneficial for good surface gloss, color performance and minimizing weld‑lines. |
Note: All data above is for reference only.