PP Maoming Petrochemical T30S
PP Maoming Petrochemical T30S Resin
Material Introduction: PP Maoming Petrochemical T30S is widely‑used drawing‑grade homopolymer polypropylene, also commonly used for injection molding. It features low melt flow rate, excellent toughness and good processability for versatile applications.
Main Applications
Woven products: Traditional and primary application, including woven bags, tarpaulins, FIBC bulk bags, carpet backing, strapping ropes. Good tensile strength and low elongation are well‑suited for these scenarios.
Injection‑molded products: Daily‑use articles and general‑purpose parts such as buckets, basins, stools and toys. Its favorable flow property adapts to injection‑molding processing.
Films & fibers: Used for tear‑film, monofilaments and spinning fibers.
Other fields: Can be modified to satisfy application requirements with higher performance standards.
Performance Parameters
| Performance Category | Test Item | Typical Value | Test Condition / Reference Standard | Remarks & Interpretation |
|---|---|---|---|---|
| Physical Properties | Density | ~0.90‑0.91 g/cm³ | General range | Low‑MFR drawing‑grade homopolymer PP |
| Melt Flow Rate(MFR) | 3.0±0.5 g/10min (premium/first‑grade), 3.0±0.9 g/10min (qualified grade) | 230℃/2.16kg, ASTM D1238 (reference) | ‑ | |
| Isotactic Index | ≥96.0 % | GB/T 2412 (reference) | ‑ | |
| Cleanness | ≤5(premium), ≤10(first‑grade), ≤20(qualified) pcs/kg | Enterprise standard | ‑ | |
| Mechanical Properties | Tensile Yield Strength | ≥32MPa(premium), ≥31MPa(first‑grade), ≥30MPa(qualified) | ASTM D638 (reference) | ‑ |
| Flexural Modulus | ≥1200MPa(premium), ≥1150MPa(first‑grade), ≥1100MPa(qualified) | ASTM D790 (reference) | ‑ | |
| Izod Notched Impact Strength | ≥39J/m(premium), ≥36J/m(first‑grade), ≥32J/m(qualified) (23℃) | ASTM D256 (reference) | ‑ | |
| Rockwell Hardness(R scale) | ≥90 R(premium), ≥85 R(first‑grade), ≥80 R(qualified) | ASTM D785 (reference) | ‑ | |
| Other Properties | Powder Ash Content | ≤0.02 % | ASTM D5630 (reference) | ‑ |
Processing Parameters
| Processing Item | Reference Range | Remarks & Instructions |
|---|---|---|
| Drying Treatment | Normally not required | PP water absorption approx.0.01%‑0.04%. Drying is unnecessary under proper storage. Dry at 80‑100 ℃ for 1‑2 h if material gets damp. |
| Barrel Temperature | 200‑280℃ | Homopolymer PP melting point:165‑170℃. Zone example: rear zone 160‑180℃；middle zone 180‑210℃；front zone 200‑230℃. Do not exceed 275 ℃ to prevent material degradation. |
| Mold Temperature | 40‑80℃ | Recommended:50℃. Higher mold temperature improves surface gloss, dimensional stability and crystallinity yet increases cooling time and shrinkage rate. Lower mold temperature shortens cycle time but may cause poor surface appearance and warpage. |
| Injection Pressure | 70‑120 MPa | Adjust based on flow length and part structure. PP melt viscosity is sensitive to shear rate; raising injection pressure is usually more effective to improve flowability than raising temperature. |
| Holding Pressure | 30%‑60% of injection pressure | Sufficient holding pressure reduces shrinkage and sink marks. Avoid overly long holding time to prevent excessive internal stress. |
| Injection Speed | Medium‑high speed | High‑speed injection helps reduce internal stress. Reduce injection speed or raise melt temperature if surface defects such as gas marks appear. |
| Back Pressure | 0.5‑1.0 MPa | Moderate back‑pressure improves melt homogenization and venting, not mandatory. |
| Screw Speed | 50‑100 rpm | Avoid excessive screw speed to prevent shear‑induced overheating. |
Disclaimer: All above data is for reference only.