PP Maoming Petrochemical Z30S Resin

Material Introduction: PP Maoming Petrochemical Z30S is fiber‑grade homopolymer polypropylene resin, characterized by high melt‑flow property and high mechanical strength.

Main Applications

Textile & packaging: packing ropes, straps, luggage belts, automotive safety belts, mattress edge binding.

Tobacco tow: tobacco tow for cigarette filter tips.

Non‑woven fabrics: suitable for non‑woven forming processes.

Performance Parameters

Performance Category	Test Item	Test Condition	Superior‑grade Value	Unit	Reference Standard	Remarks & Interpretation
Basic Properties	Melt Flow Rate(MFR)	‑	25.0±3.0	g/10 min	‑	Fiber‑grade high‑flow homopolymer PP
	Density	‑	0.833	g/cm³	ASTM D1505	‑
Mechanical Properties	Tensile Yield Strength	‑	≥32	MPa	‑	‑
	Izod Notched Impact Strength	23℃	≥28	J/m	‑	‑
Thermal Properties	Heat‑Distortion Temperature	0.45 MPa, non‑annealed	124	℃	ASTM D648	‑
	Vicat Softening Temperature	‑	169	℃	ASTM D1525	‑
Other Properties	Isotacticity	‑	≥96	%	‑	‑
	Cleanness	‑	≤5	pcs/kg	‑	‑
	Powder Ash Content	‑	≤0.02	%	‑	‑

Processing Parameters

Processing Technology	Recommended Parameters	Remarks
BCF Spinning Process	Spinning temperature:230‑290℃；Quench‑air temperature:15℃；Quench‑air velocity:1‑1.2 m/min；Quench‑air humidity:50‑70%	Controlling quench‑air humidity helps improve process stability and product quality.
Tobacco Tow Process	High‑speed spinning with low draw ratio; water‑bath drawing temperature:125‑135℃	‑
Non‑woven Forming Process	Plasticizing temperature:250‑290℃	‑
Injection‑molding Process	PP features fast cooling rate. Mold temperature ≥50℃ is recommended to avoid poor surface quality and weld‑lines. Injection temperature shall be adjusted based on melting point (~233℃) and product structure.	‑

Disclaimer: All above data is for reference only.