PP Fushun Petrochemical Z30S Resin

Material Introduction: PP Fushun Petrochemical Z30S is fiber‑grade homopolymer polypropylene resin with high melt‑flow property and good mechanical strength, mainly used for spinning applications.

Main Applications

Long‑filament polypropylene fiber, PP staple fiber.

Performance Parameters

Performance Category	Test Item	Test Condition	Test Value	Unit	Reference Standard	Remarks & Interpretation
Basic Properties	Melt Flow Rate(MFR)	‑	25.8	g/10 min	GB/T 3682	Fiber‑grade high‑flow homopolymer PP
Mechanical Properties	Tensile Yield Strength	‑	＞31.8	MPa	GB/T 1040‑2‑2006	‑
	Flexural Modulus	‑	＞1021	MPa	GB/T 9341‑2008	‑
Other Properties	Isotactic Index	‑	≥96.8	%	GB/T 2412	‑
	Yellow Index	‑	≤‑1.7	△Y.I.	HG/T 3862‑2006	‑
	Colored Particles	‑	≤5	pcs/kg	SH/T 1541‑2006	‑
	Over‑size & Under‑size Pellets	‑	≤5	g/kg	SH/T 1541‑2006	‑
	Snake‑skin & Tailing Pellets	‑	≤5	pcs/kg	SH/T 1541‑2006	‑
	Fish‑eye (0.8 mm)	‑	＜6	pcs/1520cm²	Q/SY FH0501 6.9	‑
	Fish‑eye (0.4 mm)	‑	＜14	pcs/1520cm²	Q/SY FH0501 6.9	‑
	Pellet Ash Content	‑	≤0.02	%	GB/T 9345	‑

Processing Parameters

Processing Technology	Recommended Parameters	Remarks
Spinning Process(Main intended use)	For specific spinning parameters such as temperature and draw ratio, please consult the manufacturer directly.	This grade is designed primarily for spinning.
Injection‑molding Process(General PP reference)	Barrel temperature:180‑220℃；Mold temperature:40‑80℃；Injection pressure:70‑100 MPa；Injection speed:medium‑high speed	Adjust according to product structure and mold condition. High‑flow property suits thin‑wall and complex‑geometry parts.

Disclaimer: All above data is for reference only.