MABS Chi Mei PA‑758R

MABS Chi Mei PA‑758R is a transparent‑ABS resin with excellent transparency, superior chemical resistance, relatively high rigidity and outstanding impact resistance.

Main Applications

Home‑appliance: air‑conditioner panels, washing‑machine tops, vacuum‑cleaner housings. 3C products: mobile‑phone shells, computer peripheral housings. Automotive accessories: instrument panels, center consoles. Consumer goods: cosmetic & health‑product packaging, high‑transparent toys and stationery.

Physical Properties

Property Category	Test Item	Test Condition	Test Standard	Data	Unit
Physical Properties	Density	23°C	ASTM D792 / ISO 1183	1.07‑1.08	g/cm³
	MFR	200°C / 5.0 kg	ASTM D1238	2.0‑3.0	g/10 min
	MFR	200°C / 10.0 kg	Internal method	2.2	cm³/10 min
	Light transmittance	1/8"	ASTM D1003	89	%
	Haze	1/8"	ASTM D1003	5.0	—
Mechanical Properties	Tensile strength(yield)	—	ASTM D638	45.0	MPa
	Flexural strength	—	ASTM D790	58.8‑61.7	MPa
	Flexural modulus	—	ASTM D790	2450	MPa
	Izod notched impact strength	23°C, 1/8"	ASTM D256	16	kg·cm/cm
	Charpy notched impact strength	23°C	ISO 179	16	kJ/m²
Thermal Properties	HDT	1.8 MPa, unannealed	ASTM D648	86‑88	°C
	Vicat softening temperature	—	ASTM D1525	102‑105	°C
Flame Retardancy	UL 94 rating	1.60 mm	UL 94	HB	—

Injection Molding Parameters

Process Stage	Parameter	Recommended Value	Unit
Pre‑drying	Drying temperature	80‑85	°C
	Drying time	2‑4	h
Barrel temperature	Rear (feed zone) temperature	180‑220	°C
	Middle (compression zone) temperature	190‑230	°C
	Front (metering zone) temperature	190‑230	°C
	Nozzle temperature	185‑235	°C
	Mold temperature	30‑70	°C
Injection Parameters	Injection pressure	50‑80	kg/cm²
	Hold‑on pressure	20‑50	kg/cm²
	Back pressure	5‑10	kg/cm²
	Screw speed	—	rpm

Note: All information above is for reference only!