MABS LG Chem TR‑530F

MABS LG Chem TR‑530F is a transparent resin combining good transparency, outstanding impact resistance, favorable toughness and processing flowability.

Main Applications

Electrical‑electronic: LCD optical components, home‑appliance control panels for refrigerators & washing machines, housings for mobile phones & tablets, CD sheets, switches, telephone housings. Automotive parts: instrument panels, consoles, interior trims, lamp outer covers. Consumer goods & building materials: artificial nail material, transparent containers (water bottles, food containers), home decorations, building‑material articles.

Physical Properties

Property Category	Test Item	Test Condition	Test Standard	Data	Unit
Physical Properties	Density	23°C	ASTM D792	1.05‑1.06	g/cm³
	MFR	220°C / 10.0 kg	ASTM D1238	10‑15	g/10 min
	Molding shrinkage	—	ASTM D955	0.4‑0.7	%
Mechanical Properties	Tensile strength(yield)	—	ASTM D638	32.4	MPa
	Flexural strength	—	ASTM D790	49.0	MPa
	Flexural modulus	—	ASTM D790	1470‑1860	MPa
	Izod notched impact strength	23°C, 3.20 mm	ASTM D256	240	J/m
	Elongation at break	—	ASTM D638	40‑50	%
	Rockwell hardness	—	ASTM D785	88	R‑scale
Thermal Properties	HDT	1.8 MPa, unannealed	ASTM D648	74.0‑74.4	°C
Optical Properties	Light transmittance	1/8"	ASTM D1003	86‑89	%
	Haze	1/8"	ASTM D1003	3.0‑3.3	%

Injection Molding Parameters

Process Stage	Parameter	Recommended Value	Unit
Pre‑drying	Drying temperature	80‑90	°C
	Drying time	2.0‑4.0	h
Barrel temperature	Rear temperature	200‑220	°C
	Middle temperature	210‑230	°C
	Front temperature	220‑240	°C
	Nozzle temperature	220‑240	°C
	Mold temperature	50‑70	°C
Screw Parameters	Back pressure	29.4‑58.8	MPa
	Screw speed	＜80	rpm

Note: All information above is for reference only!