PC/ABS SABIC C1100

PC/ABS SABIC C1100 is a well‑balanced alloy material. It combines the mechanical strength, heat resistance and UV‑resistance of polycarbonate (PC) with excellent processing flowability of ABS.

Main Applications

Automotive Industry: automotive interior and exterior parts such as instrument panels, pillar trims, instrument panel covers, grilles, wheel covers.

Electrical‑Electronic: housings and internal components for notebooks, desktops, copiers, printers and other business equipment; electrical appliances, lawn‑and‑garden machinery.

Telecommunications: mobile‑phone housings & accessories, smart cards (SIM‑cards).

Home Appliances: internal and external parts for washing machines, hair dryers, microwave ovens.

Physical Properties

Property Category	Test Item	Test Standard	Data	Unit
Physical Properties	Density / Specific Gravity	ASTM D792	1.12‑1.14	g/cm³
	Melt Flow Rate (MFR)	260°C/5.0 kg, ASTM D1238	8	g/10 min
	Mold Shrinkage (3.20 mm)	ASTM D955	0.5‑0.7	%
	Water Absorption	ASTM D570	0.1	%
Mechanical Properties	Tensile Strength (Yield)	ASTM D638	55‑56	MPa
	Elongation at Break	ASTM D638	30‑150	%
	Flexural Strength	ASTM D790	65‑86	MPa
	Flexural Modulus	ASTM D790	2300‑2343	MPa
	Izod Notched Impact Strength (23°C)	ASTM D256	500‑640	J/m
	Rockwell Hardness (R‑Scale)	ASTM D785	—	—
Thermal Properties	Heat‑Distortion Temperature (1.8 MPa, unannealed)	ASTM D648	100‑107	°C
	Heat‑Distortion Temperature (0.45 MPa, unannealed)	ASTM D648	115‑123	°C
	Vicat Softening Temperature	ASTM D1525	—	°C
Flame Retardancy	UL 94 Rating	UL 94	HB	—

Processing Parameters

Process Parameter	Unit	Recommended Value / Range
Drying Treatment
Drying Temperature	°C	90‑110
Drying Time	h	2‑4
Recommended Moisture Content	%	< 0.04
Injection Molding Temperature
Melt Temperature	°C	230‑300
Mold Temperature	°C	50‑100
Injection Parameters
Injection Pressure	—	Depends on molded parts
Injection Speed	—	As high as possible

Note: All information above is for reference only!