PC/ABS SABIC C1200HF
PC/ABS SABIC C1200HF
PC/ABS SABIC C1200HF is a high‑flow, high‑temperature‑resistant alloy material featuring high‑impact resistance and good surface appearance.
Main Applications
Consumer Electronics: ultra‑thin mobile‑phone middle frames, TWS earphone charging cases, notebook hinge supports.
Automotive Smart Cockpit: vehicle touch‑panel brackets, HUD projector housings.
Home Appliances: TV panel bezels, washing‑machine parts, hair dryers.
Physical Properties
| Property Category | Test Item | Test Standard | Data | Unit |
|---|---|---|---|---|
| Physical Properties | Density | ISO 1183 / ASTM D792 | 1.15 | g/cm³ |
| Melt Volume‑Flow Rate (MVR) | 260°C/5.0 kg, ISO 1133 | 22.0 | cm³/10min | |
| Melt Flow Rate (MFR) | 260°C/5.0 kg, ASTM D1238 | 19.0 | g/10 min | |
| Mold Shrinkage (Flow) | Internal Method | 0.50‑0.70 | % | |
| Water Absorption (Saturated, 23°C) | ISO 62 | 0.60 | % | |
| Mechanical Properties | Tensile Modulus | ISO 527‑2/1 | 2400 | MPa |
| Tensile Stress (Yield) | ISO 527‑2/50 | 55.0 | MPa | |
| Flexural Modulus | ISO 178 | 2300 | MPa | |
| Flexural Stress | ISO 178 | 80.0 | MPa | |
| Izod Notched Impact Strength (23°C) | ISO 180/1A | 40‑50 | kJ/m² | |
| Rockwell Hardness (R‑Scale) | ISO 2039‑2 | 115 | — | |
| Thermal Properties | Heat‑Distortion Temperature (1.8 MPa) | ISO 75‑2/Ae | 108 | °C |
| Heat‑Distortion Temperature (0.45 MPa) | ISO 75‑2/Be | 128 | °C | |
| Vicat Softening Temperature | ISO 306/B120 | 134 | °C | |
| Relative Temperature Index (RTI Elec) | UL 746 | 105 | °C | |
| Electrical Properties | Volume Resistivity | IEC 60093 | > 1.0E+15 | Ω·cm |
| Dielectric Strength (0.800 mm) | IEC 60243‑1 | 35 | kV/mm | |
| Comparative Tracking Index (CTI) | IEC 60112 | 250 | V | |
| Flame Retardancy | UL 94 Rating (1.20 mm) | UL 94 | HB | — |
Processing Parameters
| Process Parameter | Unit | Recommended Value / Range |
|---|---|---|
| Drying Treatment | ||
| Drying Temperature | °C | 60‑90 |
| Drying Time | h | 2.0‑8.0 |
| Recommended Moisture Content | % | ≤ 0.20 |
| Injection Molding Temperature | ||
| Rear Barrel Temperature | °C | 220‑250 |
| Middle Barrel Temperature | °C | 230‑260 |
| Front Barrel Temperature | °C | 240‑270 |
| Nozzle Temperature | °C | 250‑280 |
| Melt Temperature | °C | 240‑280 |
| Mold Temperature | °C | 40‑100 |
| Screw Parameters | ||
| Back Pressure | psi | 50‑100 |
| Screw Speed | rpm | 40‑70 |
| Suggested Shot Volume | % | 30‑80 |
| Mold Parameter | ||
| Vent Depth | mm | 0.038‑0.076 |
Note: All information above is for reference only!