PC/ABS SABIC C1200
PC/ABS SABIC C1200
PC/ABS SABIC C1200 is an alloy material with balanced comprehensive performance. It combines the mechanical strength, heat resistance and UV‑resistance of polycarbonate (PC) with the excellent processing flowability of ABS.
Main Applications
Electrical‑Electronic: housings and components for electrical‑electronic products.
Automotive Industry: automotive components including interior parts.
Home Appliances: parts for home‑appliance manufacturing.
Physical Properties
| Property Category | Test Item | Test Standard | Data | Unit |
|---|---|---|---|---|
| Physical Properties | Density | ASTM D792 | 1.15 | g/cm³ |
| Mold Shrinkage (3.2 mm) | ASTM D955 | 0.5‑0.7 | % | |
| Water Absorption | ASTM D570 | Data missing | % | |
| Mechanical Properties | Tensile Strength (Yield) | ASTM D638 | 61 | MPa |
| Tensile Modulus | ASTM D638 | 2274 | MPa | |
| Elongation at Break | ASTM D638 | 150 | % | |
| Flexural Strength | ASTM D790 | 88 | MPa | |
| Flexural Modulus | ASTM D790 | 2343 | MPa | |
| Izod Notched Impact Strength (23°C) | ASTM D256 | 640 | J/m | |
| Rockwell Hardness (R Scale) | ASTM D785 | Data missing | — | |
| Thermal Properties | Heat‑Distortion Temperature (1.8 MPa) | ASTM D648 | 112 | °C |
| Heat‑Distortion Temperature (0.45 MPa) | ASTM D648 | 129 | °C | |
| Vicat Softening Temperature | ASTM D1525 | Data missing | °C | |
| UL RTI (With Impact) | UL 746B | 60 | °C | |
| UL RTI (Without Impact) | UL 746B | 60 | °C | |
| Electrical Properties | Volume Resistivity | ASTM D257 | Data missing | Ω·cm |
| Dielectric Constant (1 MHz) | ASTM D150 | Data missing | — | |
| Flame Retardancy | UL 94 Rating | UL 94 | HB | — |
Processing Parameters
| Process Parameter | Unit | Recommended Value / Range |
|---|---|---|
| Drying Treatment | ||
| Drying Temperature | °C | 90~110 |
| Drying Time | h | 2~4 |
| Recommended Moisture Content | % | < 0.04 |
| Injection Molding Temperature | ||
| Melt Temperature | °C | 230~300 |
| Mold Temperature | °C | 50~100 |
| Injection Parameters | ||
| Injection Pressure | — | Depends on molded parts |
| Injection Speed | — | As high as possible |
Note: All information above is for reference only!