PC/ABS CHIMEI(Zhenjiang) PC‑345K

PC/ABS CHIMEI(Zhenjiang) PC‑345K is a general‑purpose alloy resin. It combines the advantages of high rigidity and high‑impact resistance of polycarbonate (PC) and high flowability of acrylonitrile‑butadiene‑styrene copolymer (ABS).

Main Applications

Automotive Accessories: automotive interior parts.

Electrical‑Electronic: set‑top boxes, projectors, 3C digital products, transformers, game consoles, network‑communication products, also widely used for mobile phone housings.

General Molded Articles: computer housings and accessories.

Physical Properties

Property Category	Test Item	Test Standard	Unit	Typical Value	Property Description
Basic Physical Properties
	Density	ISO 1183	g/cm³	1.16‑1.18	Advantage for lightweight design
	Water Absorption (23℃, 24h)	ISO 62	%	0.15‑0.25	Low water absorption, good dimensional stability
	Melt Mass‑Flow Rate (MFR)	ISO 1133 (265℃/5kg)	g/10min	12‑18	High flowability, suitable for complex thin‑wall injection molding
Mechanical Properties
	Tensile Strength	ISO 527	MPa	55‑65	High rigidity, excellent tensile performance
	Elongation at Break	ISO 527	%	80‑120	Good ductility
	Flexural Strength	ISO 178	MPa	85‑95	High bending load‑bearing capacity
	Flexural Modulus	ISO 178	MPa	2300‑2600	Suitable for high‑rigidity supporting structures
	Izod Notched Impact Strength	ISO 180	kJ/m²	45‑60	Ultra‑high toughness, preferred for drop‑ and impact‑resistant applications
Thermal Properties
	Heat‑Distortion Temperature (HDT, 1.82 MPa)	ISO 75	℃	105‑115	Good stability under medium‑high temperature environment
	Vicat Softening Temperature (VST, 50N)	ISO 306	℃	120‑125	Better heat resistance than general‑purpose ABS
	Linear Thermal Expansion Coefficient	ISO 11359	10⁻⁵/K	7‑9	High compatibility for assembly with metal parts
Electrical Properties
	Dielectric Strength	IEC 60243	kV/mm	28‑35	Reliable insulation performance
	Volume Resistivity	IEC 60093	Ω·cm	>10¹⁵	Extremely high resistance, applicable for electronic housings
Flame Retardancy & Safety
	UL94 Flammability Rating	UL94	—	V‑0 (1.5 mm)	Halogen‑free flame retardant, passed strict fire‑safety certification

Processing Parameters

Process Parameter	Unit	Recommended Value / Range
Drying Treatment
Drying Temperature	°C	80.0‑90.0
Drying Time	h	2.0‑4.0
Recommended Moisture Content	%	< 0.020
Injection Molding Temperature
Rear Barrel Temperature	°C	230‑280
Middle Barrel Temperature	°C	240‑290
Front Barrel Temperature	°C	250‑300
Nozzle Temperature	°C	250‑300
Melt Processing Temperature	°C	250‑300
Mold Temperature	°C	60‑90
Mold Parameter
Vent Groove Depth	mm	0.030‑0.075

Note: All information above is for reference only!