PPS Polyplastics 1130T6

PPS Polyplastics (Japan) 1130T6

PPS Polyplastics 1130T6 is a 30% glass‑fiber‑reinforced polyphenylene sulfide (PPS) engineering plastic. It delivers excellent performance in high‑impact resistance, heat resistance, dimensional stability and flame retardancy.

Main Applications

Automotive components: water pumps, various electrical equipment parts.

Electrical‑Electronic Industry: lamp holders and similar parts.

Equipment: functional components for office equipment and audio‑visual devices.

Physical Properties

Property Category	Test Item	Test Condition	Test Standard	Test Data	Unit
Physical Properties	Density / Specific Gravity	—	ISO 1183	1.52	g/cm³
	Water Absorption	23℃, 24hr	ISO 62	0.01‑0.06	%
	Melt Viscosity	310℃, 1000/sec	ISO 11443	400	Pa·s
	Molding Shrinkage‑Flow Direction	80℃×2 mmt	—	0.3	%
	Molding Shrinkage‑Transverse Direction	80℃×2 mmt	—	0.7	%
Mechanical Properties	Tensile Strength	23℃	ISO 527‑2	155	MPa
	Elongation at Break	23℃	ISO 527‑2	2.3	%
	Flexural Strength	23℃	ISO 178	220	MPa
	Flexural Modulus	23℃	ISO 178	8800	MPa
	Charpy Notched Impact Strength	23℃	ISO 179/1eA	12	kJ/m²
	Rockwell Hardness	—	ISO 2039‑2	85	M Scale
Thermal Properties	Heat‑Distortion Temperature (HDT)	1.8 MPa	ISO 75‑1	255	℃
	Linear Thermal Expansion Coefficient‑Flow Direction	—	ISO 11359‑2	2.0	×10⁻⁵/℃
	Linear Thermal Expansion Coefficient‑Transverse Direction	—	ISO 11359‑2	4.0	×10⁻⁵/℃
Electrical Properties	Volume Resistivity	—	IEC 60093	8×10¹⁵	Ω·cm
	Dielectric Strength	3.00 mm	IEC 60243‑1	18	kV/mm
	Dielectric Constant	1kHz / 1MHz	IEC 60250	3.9	—
	Dielectric Loss Tangent	1kHz / 1MHz	IEC 60250	0.003 / 0.004	—
	Arc Resistance	—	ASTM D495	123	s
	Comparative Tracking Index (CTI)	—	IEC 60112	125	V
Flame Retardancy	UL Flammability Rating	1.6 mm	UL 94	V‑0	—

Injection Molding Parameters

Processing Stage	Parameter Item	Reference Value	Unit
Drying	Drying Temperature	130	°C
	Drying Time	3	h
Injection Temperature	Rear Barrel Temperature	300‑320	°C
	Middle Barrel Temperature	290‑310	°C
	Front Barrel Temperature	220‑260	°C
	Nozzle Temperature	290‑300	°C
	Melt Temperature	235‑280	°C
Mold & Pressure	Mold Temperature	60‑80	°C
	Injection Pressure	60‑70	MPa
	Screw Speed	28	rpm

Note: All information above is for reference only!