POE LG Chem LC565
POE LG Chem LC565
POE LG Chem LC565 is an ethylene‑1‑butene polyolefin elastomer produced via metallocene catalyst and solution‑process technology. It significantly improves impact performance of plastics, featuring excellent flexibility and high‑filler compatibility.
Main Applications
General‑Plastic Toughening: Widely used for modification and toughening of PP and PE. Automotive Parts: Interior & exterior parts including bumpers, fenders, steering wheels and cushions. Other Fields: Wire & cable, footwear materials, industrial hoses, conveyor belts, home‑appliance parts and toys.
Physical Properties
表格
| Category | Property Item | Value | Test Standard |
|---|---|---|---|
| Physical | Density | 0.865 g/cm³ | ASTM D1505 / ASTM D792 |
| MFR (190 °C, 2.16 kg) | 5.0 g/10 min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 121 °C) | 8 MU | ASTM D1646 | |
| Mechanical | Tensile Strength at Break | 1.8 MPa | ASTM D638 |
| Flexural Modulus | 8 MPa | — | |
| Elongation at Break | 550 % | ASTM D638 | |
| Tear Strength | 20 kN/m | ASTM D624 | |
| Shore A Hardness | 54 | ASTM D2240 | |
| Thermal | Melting Temperature | 36 °C | — |
Processing Guidelines
表格
| Processing Step | Parameter Suggestion | Remarks |
|---|---|---|
| Compound Pelletizing | Blend with base resin via twin‑screw extruder | Control temperature to avoid material degradation |
| Injection Molding | Melt temperature：160‑220 ℃；Mold temperature：30‑60 ℃ | Fine‑tune according to base resin |
Note: All data above are for reference only.