PLA US NatureWorks 3052D

NatureWorks 3052D (USA)

NatureWorks 3052D is a high‑flow, transparent, general‑purpose injection‑molding grade biodegradable PLA resin, specially designed for disposable transparent articles.

Main Applications

Tableware & Utensils: Knives, forks, spoons, cold‑drink cups, plates and dishes. Outdoor novelty items: Festival decorations, event souvenirs, etc. Laboratory & modification base resin: Frequently used as matrix resin for composite material development in R&D.

Property Specifications

Category	Property	Test Standard	Typical Value	Unit
Basic Physical Properties	Specific gravity / Density	ASTM D792	1.24	g/cm³
	Melt Flow Rate (210 °C, 2.16 kg)	ASTM D1238	14	g/10min
	Mold shrinkage‑flow direction	ASTM D955	0.30‑0.50	%
Mechanical Properties	Tensile yield strength	ASTM D638	62	MPa
	Elongation at break	ASTM D638	3.5	%
	Flexural strength	ASTM D790	108	MPa
	Flexural modulus	ASTM D790	3600 (3550‑3830)	MPa
	Izod notched impact strength	ASTM D256	16	J/m
Thermal Properties	Melting point (crystallization peak)	ASTM D3418	145‑160	°C
	Glass‑transition temperature (Tg)	ASTM D3418	55‑60	°C
	Heat‑deflection temperature (0.46 MPa / 66 psi)	ASTM E2092	55	°C
	Melt processing temperature	‑	~200	°C

Injection‑Molding Processing Parameters

Processing Stage	Parameter	Recommended Range	Unit
Pre‑treatment	Drying temperature	55‑60	°C
	Drying time	2‑4	h
	Recommended dryer	Dehumidifying dryer (moisture ≤0.025%)	‑
Injection molding	Rear barrel temperature	160‑170	°C
	Middle barrel temperature	190‑200	°C
	Front barrel / nozzle temperature	200‑205	°C
	Melt temperature	195‑205 (max. 210 °C)	°C
	Mold temperature	20‑40	°C
Other settings	Injection pressure	Medium‑high	‑
	Back pressure	0.3‑0.7	MPa
	Screw speed	100‑175	rpm

All above data are for reference only.